Published Data
These pages provide an access point to data contained in CCFE published journal papers. By selecting a paper, and then a specific figure or table, you can request the related underlying data if it is available for release.
Publication Figures
Publication Date:
2018-04-10
First Author:
Alexandra Cackett
Title:
Using spherical indentation to measure the strength of copper-chromium-zirconium
Paper Identifier:
Search the list of Figures using keywords (case insensitive):
To drill down to information on Data within a published figure, select a table cell where the figure's number of Data Items > 0
Use the Download buttons to download information on each listed figure, e.g. the image file and how it was created
| Figure Reference | Title | Description | Number of Figure Data Items | Identifier | Download Figure Details | ||
|---|---|---|---|---|---|---|---|
| Figure 1 | Fig. 1 – Vicker’s hardness | Vickers hardness as a function of heat treatment temperature for CuCrZr samples. | 0 | CF/17/263 | Download | ||
| Figure 2 | Fig. 2 – EDS chemical maps | EDS chemical analysis Cr maps for (a) AR, (b) 400 °C, (c) 480 °C, and (d) 550 °C heat treated CuCrZr. | 0 | CF/17/264 | Download | ||
| Table 1 | Table 1 – Precipitate diameter and spacings | Average precipitate diameter and spacings for all samples. | 0 | CF/17/265 | Download | ||
| Figure 3 | Fig. 3 – Indentation stress-strain and elastic modulus plots for AR CuCrZr | Indentation results for AR (solution annealed) CuCrZr using five indenters of different radii; (a) indentation stress and (b) elastic modulus as a function of indentation strain. | 0 | CF/17/266 | Download | ||
| Figure 4 (a) | Fig. 4(a) – Indentation pressure vs tip radius | Hardness calculated at first available data point in stress-strain plot. | 0 | CF/17/267 | Download | ||