These pages provide an access point to data contained in CCFE published journal papers.  By selecting a paper, and then a specific figure or table, you can request the related underlying data if it is available for release.

« Back

Publication Figures

Publication Date:
2016-02-10

First Author:
Michael Gorley

Title:
An analysis of the microstructure of spark plasma sintered and hot isostatically pressed V-4Cr-4Ti-1.8Y-0.4Ti3SiC2 alloy and its thermal stability

Paper Identifier:
CP/16/100

Search the list of Figures using keywords (case insensitive):

To drill down to information on Data within a published figure, select a table cell where the figure's number of Data Items > 0
Use the Download buttons to download information on each listed figure, e.g. the image file and how it was created

Figure Reference Title Description Number of Figure Data Items Identifier Download Figure Details
Figure 3. Figure 3. EBSD data of as-processed material Figure 3. EBSD data of as-processed material (a) Inverse pole figure (IPF) map of as-processed material, (b) band contrast image of (a), (c) high resolution TKD map of fine-grained region, (d) {111} pole figure of (a), (e) {111} pole figure of a region close to (a). (f) Distribution of disorientation axes for pole figures (d) dark and (e) hashed. Note, Z is the compression axis during SPS. 2 CF/16/103 Download
Figure 2. Figure 2. Hardness of as-processed and heat treated material as a function of heat treatment temperature. Figure 2. Hardness of as-processed and heat treated material as a function of heat treatment temperature. 0 CF/16/104 Download
Figure 4 Figure 4. EBSD data of heat treated material Figure 4. EBSD data of heat treated material. (a) (d) (g) IPF maps of material heat treated to 800, 1000 and 1200°C, respectively. (b) (e) (h) band contrast maps of maps (a), (d) and (g), respectively. (c) (f) (i) {111} pole figures of maps (a), (d) and (g), respectively. Note, Z is the compression axis during SPS. 3 CF/16/105 Download